1. Diferans fondamantal
| Posesyon | Hastelloy C276 (UNS N10276) | Nerjaveèi asye 316 (UNS S31600) |
|---|---|---|
| Kalite materyèl | Alyaj nikèl-chromium-molibdèn | Austenitik asye pur |
| Kle eleman alyaj | Ni (57%), Cr (16%), MO (16%) | Fe (65%), Cr (17%), Ni (12%), MO (2.5%) |
| Pri (Indexed) | 400-500 | 100 (debaz) |
2. Konparezon rezistans korozyon
Rezistans chimik
| Alantou | C276 Pèfòmans | SS316 Pèfòmans |
|---|---|---|
| Asid idroklorik (kloridrat) | Ekselan (tout konsantrasyon) | Poor (>1% nan RT) |
| Asid silfirik (h₂so₄) | Bon (jiska 70%) | Limite (<10%) |
| Asid fosforik | Eselan | Bon |
| Klorid (NaCl) | Eksepsyonèl (pa gen okenn SCC*) | Prone to SCC (>50 degre) |
| Asid oksidant | Eselan | Jis |
*SCC=Estrès Kowozyon Cracking
Pitting\/fant korozyon
C276: Pren **=~ 69 (trè rezistan)
SS316: Pren=~ 26 (rezistans modere)
** pren=Pitting rezistans nimewo ekivalan (cr + 3. 3mo + 16 n)
3. Pwopriyete mekanik
| Posesyon | C276 | SS316 |
|---|---|---|
| Fòs rupture | 790 MPa (min) | 515 MPa (min) |
| Sede fòs | 415 MPa (min) | 205 MPa (min) |
| Elongasyon | 40% (min) | 40% (min) |
| Dite (Brinell) | 209 Max | 217 Max |
| Densite | 8.89 g\/cm³ | 8. 0 g\/cm³ |
4. kapasite tanperati
| Kondisyon | C276 | SS316 |
|---|---|---|
| Max kontinyèl | 1093 degre (oksidant) | 925 degre |
| Tanperati min | -196 degre | -270 degre |
| Eskalad rezistans | Eselan | Jis (pi wo a 600 degre) |
5. Konsiderasyon fabwikasyon
| Trete | C276 | SS316 |
|---|---|---|
| Akizasyon | Mande pou filler ki baze sou Ni (Ernicrmo -4) | Creole SS filler (ER316) |
| Machinabilite | Difisil (20% nan 316 vitès) | Modere (comparativement pi fasil) |
| Travay redi | Sevè | Modere |
| Fòm | Mande pou rkwir | Bon Fwad Formability |
6. Aplikasyon endistri yo
| Endistri | C276 Itilizasyon tipik | SS316 Itilizasyon tipik |
|---|---|---|
| Chimik | Réacteurs, scrubbers, sistèm kloridrat | Tank, kanalizasyon, tiyo |
| Lwil & gaz | Eleman downhole, sèvis tounen | Platfòm lanmè, tuyaux |
| Famasetik | Sistèm CIP\/SIP | Pwosesis veso yo |
| Maren | Echanjeur chalè dlo lanmè | Ekipman bato, pyès ki nan konpitè |
| Pouvwa | Sistèm FGD | Sistèm kondansasyon |
7. Lè yo chwazi ki?
Chwazi C276 lè:
✔ Manyen asid melanje (kloridrat + h₂so₄)
✔ Chloride concentration >1000 ppm
✔ Temperature >600 degre ak gaz korozivite
✔ NACE MR0175 SÈVIS SOU
Chwazi SS316 lè:
✔ Bidjè contrainte
✔ Sèlman modere koroziv prezan (ph 4-9)
(Aplikasyon pou kriyojenik (<-100°C)
✔ Fabrication wo-volim ki nesesè
8. Pri-benefis analiz
C276: 4-5 x pi chè pase SS316, men dire 10x pi long nan anviwònman piman bouk
Pri lifecycle: C276 souvan pi bon mache alontèm nan plant chimik\/petrochimik
9. Mòd echèk komen
| Materyo | Echèk tipik | Prevansyon |
|---|---|---|
| C276 | Klori-pwovoke Pitting (ra) | Bon rkwir |
| SS316 | SCC, Crevice korozyon | Avoid chlorides >50 degre |