Monel K500 vs Inconel 718-Sa yo se tou de pèfòmans-wo alyaj nikèl, men yo diferan siyifikativman nan konpozisyon, fòs mekanik, rezistans korozyon, ak aplikasyon pou tipik. Isit la nan yon konparezon detaye:
🔹 konpozisyon chimik
| Eleman | Monel K500(UNS N05500) | Inconel 718(UNS N07718) |
|---|---|---|
| Nikèl (Ni) | 63% min | 50–55% |
| Copper (CU) | 27–33% | Mwens pase oswa egal a 0. 30% |
| Iron (Fe) | Mwens pase oswa egal a 2. 0% | Res |
| CHROMIUM (CR) | Mwens pase oswa egal a 0. 25% | 17–21% |
| Molibden (MO) | - | 2.8–3.3% |
| Al + ti (aje eleman) | 2.3–3.15% konbine | {{0}}. 65% ti, 0.9% al |
| Niobium (NB) | - | 4.75–5.5% |
(Pwopriyete mekanik (laj-fè tèt di toujou)
| Posesyon | Monel K500 | Inconel 718 |
|---|---|---|
| Fòs rupture | Jiska 160 ksi (1100 MPa) | Jiska 200 ksi (1375 MPa) |
| Sede fòs | Jiska 110 ksi (758 MPa) | Jiska 170 ksi (1170 MPa) |
| Rez nan | Jiska 45 HRC | Jiska 44 HRC |
| Max sèvis temp. | ~ 600 degre (1110 degre F) | ~ 700 degre (1300 degre f) |
🔹 Rezistans korozyon
| Alantou | Monel K500 | Inconel 718 |
|---|---|---|
| La dlo | Eselan | Bon |
| Asid (kloridrat, H2SO4) | Bon (espesyalman diminye asid) | Ekselan (espesyalman oksidant) |
| Rezistans oksidasyon | Modere | Eselan |
🔹 Aplikasyon
| Endistri | Monel K500 | Inconel 718 |
|---|---|---|
| Maren | Rasin pwopilsè, rasin ponp | Mwens komen |
| Lwil & gaz | Fè egzèsis kolye, valv taye, zouti downhole | High-presyon tib, Fastener |
| Avyon | Springs, Fastener | Disk turbine, pati motè jè |
| Pwosesis chimik | Ponp, tiyo | Tib superheater, veso presyon |
🔹 Rezime konparezon
| Kritè | Monel K500 | Inconel 718 |
|---|---|---|
| Fòs (ki gen laj) | Wo | Trè wo |
| Rezistans korozyon | Pi bon nan dlo lanmè | Siperyè nan wo-tanperati ak asid anviwònman |
| Koute | Bese | Pi wo |
| Machinabilite | Modere | Difisil (travay solid byen vit) |
| Soudedabilite | San Patipri (mande pou swen) | Ekselan (sitou ak filler apwopriye) |
🔧 SSM ka bay:
Monel K500: Branch, èl, ekipman, Fastener
Inconel 718: Plak, ba, bag, forgings koutim